LR6 battery.What should we pay attention to in the winding process of 18650 lithium battery?

What should we pay attention to in the winding process of 18650 lithium battery?

1. Humidity control <1% RH Purpose: Beware of water absorption during the winding process of the positive and negative electrode sheets, resulting in zero voltage, self-discharge, and poor cycle performance;


Method: Calculate the dew point value and temperature value to obtain the temperature and humidity value;


2. Dust control &le;100,000pc/ft3 (test particle size is 0.5um)


Purpose: To prevent dust from being involved in the electrode assembly during winding, causing battery core short circuit, overheating, fire, self-discharge and other defects;
Low temperature lithium iron phosphate battery 3.2V 20A -20℃ charging, -40℃ 3C discharge capacity ≥70%

Charging temperature: -20~45℃ -Discharge temperature: -40~+55℃ -40℃ Support maximum discharge rate: 3C -40℃ 3C discharge capacity retention rate ≥70%
Click for details

Method: Use dust detector;


3. Abnormal cutting burrs


Process requirements: pole piece &le;8um; pole lug burr &le;12um; test method: randomly select 1 PCS battery cells for dissection during the first inspection of each machine in each shift, and test the front and rear ends of the positive and negative pole pieces and the positive electrode according to the "Burr Test Operation Instruction Book" , Negative tab cutting burrs.


Adverse effects: The burrs on the pole pieces or tabs exceeding the process requirements may cause the burrs to pierce the diaphragm, short-circuit the positive and negative poles, cause the battery core to overheat, and may explode in severe cases, posing serious safety hazards.


18650 lithium ion battery winding steps
Low temperature and high energy density 18650 3350mAh-40℃ 0.5C discharge capacity ≥60%

Charging temperature: 0~45℃ Discharge temperature: -40~+55℃ Specific energy: 240Wh/kg -40℃ Discharge capacity retention rate: 0.5C Discharge capacity ≥ 60%
Click for details

4. Difference in overturning of positive and negative electrode plates


Process requirements: The alignment of positive and negative electrode plates is 0.75?.55mm


The alignment between the negative electrode sheet and the separator is 1?.5mm


Testing method: After changing the roll, random inspection continues with 3PCS cells. Test the alignment according to the "X-RAY Operation Instruction Manual". Adverse effects: 1) The alignment of the positive and negative electrodes exceeds the process specifications, which may cause the negative electrodes not to wrap the positive electrodes, and the positive electrodes are not wrapped around the battery core. During the charging process, the lithium ions released from the positive electrode cannot find the corresponding graphite to embed, causing free lithium ions in the battery core to accumulate on the negative electrode and form dendrites. The dendrites pierce the separator, causing an internal short circuit and posing a safety hazard.


2) If the alignment between the negative electrode sheet and the separator exceeds the process standard, the negative electrode sheet may be squeezed and deformed, and the negative electrode material on the electrode sheet may partially fall off. During the charging process, the battery core will expand, and the powder will pierce the separator, causing an internal short circuit of the positive and negative electrodes, causing safety hazards. hidden danger;


5. The pole piece overturning difference in the winding direction (the length of the outer layer of negative electrode and super positive electrode material, the length of the inner layer of negative electrode and super positive electrode material) test method: every 2 hours, each winding machine randomly inspects the dissection of 3 PCS cells, and uses an eyepiece and a ruler to measure the two Kind of overturning difference size.


Adverse effects: It may cause the negative electrode sheet not to wrap the positive electrode sheet. During the charging process of the battery cell, the lithium ions released from the positive electrode cannot find the corresponding graphite to embed, causing free lithium ions in the battery core to accumulate on the negative electrode and form dendrites. Dendrites pierce the diaphragm and cause an internal short circuit, posing a safety hazard.


18650 lithium ion battery winding steps


6. Short circuit detection


Parameter settings (100V, 25nF250V,


250uA) Test method: use short-circuit sample detection machine during the first inspection of each shift; adverse effects: short-circuit factors such as self-discharge, heating, explosion, etc.: cutting particles, metal dust, burrs, etc. causing diaphragm holes;

Read recommendations:

R6P

What are the main differences between ternary lithium batteries and lithium iron phosphate batteries

What are the factors that affect the low-temperature performance of lithium-ion batteries

Nickel Metal Hydride No. 11 battery direct sales

polymer lithium battery